Product Details:
Payment & Shipping Terms:
|
| Name: | AZ80A Magnesium Alloy Bar | Form: | Rod / Bar / Billet |
|---|---|---|---|
| Surface: | Smooth Surface | Material: | Magnesium, Magnesium Alloy |
| Purity: | >98% | Application: | Industrial Alloying |
| Size: | Accept Custom | Certificate: | ISO9001 |
| Chemical Composition: | Mg Al Zn Mn | Produce: | Hot Roll, Casting, Extruding |
| Color: | Silvery | ||
| High Light: | AZ80A Magnesium Alloy Bar,Dissolvable Extruded Magnesium Alloy Rod,AZ80A Magnesium Alloy Rod |
||
95%-99.98% AZ80A Extruded Magnesium Alloy Bar Rod Billet for Electronics , Machinery Parts
Details:
Name: magnesium alloy bar,dissolvable magnesium bar.
Specification: Ø50mm,Ø60mm,Ø70mm,Ø80mm,Ø90mm,Ø100mm…..Or customized according to customer requirements.
AZ80A magnesium alloy is an alloy composed of magnesium and other elements added as the base. Its characteristics are: low density (about 1.8g/cm3 magnesium alloy), high specific strength, large specific modulus of elasticity, good heat dissipation, good shock absorption, greater impact load capacity than aluminum alloy, resistance to organics and alkali corrosion it is good. The main alloying elements of AZ80A are aluminum, zinc, manganese, cerium, thorium and a small amount of zirconium or cadmium.
| Hilbo magnesium alloy material Co., Ltd. | ||||||||||||||
| Quality Inspection Report | ||||||||||||||
| NO:JB/MS03-151-1236 | ||||||||||||||
| Model | Specifications | Process | Furnace No. | Chemical Composition (%) | Low power test | |||||||||
| Al | Zn | Mn | Fe | Si | Cu | Ni | Mg | Low power | Surface quality | Size | ||||
| Ø80*1000 | Extrussion | 9850 | 8.5 | 0.60 | 0.3 | 0.005 | 0.1 | 0.05 | 0.005 | Balance | OK | OK | OK | |
| AZ80A H112 |
||||||||||||||
| Magnesium alloy bar | ||||||||||||||
| Tensile strength Rm /Mpa |
Yield strength 0.2% Mpa |
Elongation at break % | ||||||||||||
| 295 | 190 | 5 | ||||||||||||
| Conclusion :Passed inspection | ||||||||||||||
Magnesium Alloy Chemical Composition:
|
Model
|
chemical component(%) |
||||||
|
Type |
Mg |
Al |
Zn |
Mn |
Si |
Fe |
Cu |
|
AX31B |
residual |
2.5-3.5 |
0.60-1.4 |
0.20-1.0 |
≤0.08 |
≤0.003 |
≤0.001 |
|
AZ61A |
|
5.8-7.2 |
0.40-1.5 |
0.15-0.50 |
≤0.10 |
≤0.005 |
≤0.005 |
|
AZ80A |
|
7.8-9.2 |
0.20-0.80 |
0.12-0.50 |
≤0.10 |
≤0.005 |
≤0.005 |
|
AZ91D |
|
8.5-9.5 |
0.45-0.90 |
0.17-0.40 |
≤0.08 |
≤0.004 |
≤0.001 |
Product Advantages:
Performance test data:
| No. | Model | Test condition | Dissolution rate mg/(cm2*h)) |
Strength of extension(MPa) | Yield strength(MPa) | Elongation (%) |
Hardness (HB) |
| 1 | HB006 | 93℃/3%KCl | 50-70 | ≥370 | ≥260 | ≥2.5 | ≥90 |
| 2 | HB006A | 93℃/3%KCl | 50-70 | ≥310 | ≥220 | ≥6.0 | ≥75 |
| 3 | HB008 | 93℃/3%KCl | 40-60 | ≥400 | ≥300 | ≥4.0 | ≥100 |
| 4 | HB008B | 93℃/3%KCl | 40-60 | ≥370 | ≥270 | ≥5 | ≥100 |
| 5 | HB008C | 93℃/3%KCl | 40-60 | ≥310 | ≥220 | ≥15 | ≥85 |
| 6 | HB012 | 93℃/3%KCl | 40-60 | ≥400 | ≥300 | ≥3.0 | ≥100 |
| 7 | HB011 | 93℃/3%KCl | 15-35 | ≥420 | ≥300 | ≥3.0 | ≥100 |
| 8 | HB016 | 93℃/3%KCl | 35-55 | ≥280 | ≥180 | ≥15 | ≥60 |
| 9 | HB017 | 93℃/3%KCl | 40-50 | ≥200 | ≥140 | ≥17 | ≥55 |
| 10 | HB018K | 50℃/0.84KCl | 50-70 | ≥240 | ≥170 | ≥12 | ≥55 |
| 11 | HB018 | 50℃/0.84KCl | 30-50 | ≥230 | ≥170 | ≥12 | ≥55 |
| 12 | HB010 | 93℃/3%KCl | 15-35 | ≥190 | ≥120 | ≥30 | ≥45 |
| 13 | HB022 | 43℃/0.05%KCl | 50-60 | ≥300 | ≥200 | ≥5.0 | ≥75 |
| 14 | HB023 | 43℃/0.05%KCl | 20-40 | ≥280 | ≥200 | ≥7.5 | ≥65 |
| 15 | HB024 | 43℃/0.05%KCl | 50-70 | ≥260 | ≥220 | ≥5 | ≥60 |
| 16 | HB013A | 43℃/0.05%KCl | 80-100 | ≥260 | ≥230 | ≥3.5 | ≥75 |
| 17 | HB025 | 50℃/0.84%KCl | 90-110 | ≥275 | ≥200 | ≥12 | ≥65 |
| 18 | HB026 | 93℃/3%KCl | 20-40 | ≥450 | ≥350 | ≥3.0 | ≥110 |
| 19 | HB808 | 50℃/0.84%KCl | 50-70 | ≥370 | ≥260 | ≥3.0 | ≥100 |
| 20 | HB019 | 50℃/0.84KCl | 45-65 | ≥230 | ≥180 | ≥12.0 | ≥55 |
| 21 | HB055 | 93℃/3%KCl | 130-150 | ≥220 | ≥160 | ≥12.0 | ≥55 |
| 22 | HB035 | 93℃/3%KCl | 50-100 | ≥100 | ≥60 | ≥42.0 | ≥35 |
| 23 | HBMM6 | 50℃/0.84%KCl | 70-100 | ≥260 | ≥230 | ≥10.0 | ≥60 |
| 24 | HBMM7 | 50℃/0.84%KCl | 90-120 | ≥270 | ≥240 | ≥9.0 | ≥65 |
| 25 | HBMM8 | 93℃/3%KCl | 100-150 | ≥280 | ≥250 | ≥5.0 | ≥65 |
Advantage of Hilbo Company:
Full range of product types, Ensure production capacity
We ave advanced die-casting, extrusion, forging, rolling, casting processing production line and precision testing equipment. Can produce a variety of types of magnesium alloy and magnesium alloy products, and developed a high-strength magnesium alloy extruded sheet. Through the purification of ordinary magnesium, magnesium can be raised up to 99.99% of high purity.
Cost advantage
Magnesium alloy casting production can customized as your requirement. the technical process is great, extrusion production required for a variety of bar, no need to purchase from abroad, extrusion molding products is easy molding, low energy consumption, saving production costs.
Workshop:
Testing Equipment
Certificate:
We have attained ISO9001 and ISO14001 certificates, Standardize and improve the enterprise quality management system.
FAQ:
Contact Person: Miss. Emily shi
Tel: +86 13714725615
Fax: 86-0769-82385085
AZ31B-H24 Magnesium Alloy Plate Thick High Strength Magnesium Sheet Slab
WE54 Magnesium Alloy Plate High Strength Magnesium Plate Stock Material
AZ91D AM50A AM60B Magnesium Alloy Plate AZ31B Magnesium Plate Non Magnetic
Magnesium Alloy Plate AZ31 AZ91 Mainly For Thin Plates , Extrusion And Forgings
Outdoor Survival Magnesium Fire Starter Anti Corrosion Magnesium Flint Stone
All Weather Emergency Magnesium Fire Starter 2 In 1 Magnesium Fuel Bar
Customized Logo Magnesium Fire Starter Camping Survival Flint Scraper Stone
Multifunction Emergency 2 In 1 Mag Bar Fire Starter 5.5 x 3 x 0.2 Inches